180F Agglomerated Rutile Flux For Saw

180F is a rutile agglomerated flux, active in Mn and Si, suitable for carbon steel welding in two or three passes, in single or multi-wires, at high speed with excellent bead appearance.
Excellent slag removal in fillet and root passes. In combination with AWS EH14 wire, is suitable only for fillet welding in single pass.
Good slag removal in fillet and groove welds.
Welding current: DC or AC, in single or multi-wire up to 1200 A. per wire.
Applications:
Structural steel works, Small tanks, Light boiler works, Beams, Shipbuilding and pipes, Gas cylinders.
Available in 25 kgs bag

Flux Main Chemical Composition:
CaO+CaF2+MgO=17, MnO+FeO=17, SiO2=19, Al2O3+TiO2+ZrO2=52
Basicity Index: 0.4 ca.

Filo S1
Typical Chemical Properties (As Welded)
C 0.03-0.05, Mn 0.90-1.40, Si 0.60-1.00, Cu <0.35, S 0.020, P 0.030

Typical Mechanical Properties (As Welded)
Tensile Strength >520 MPa
Yield Strength >400 MPa
Elongation in 2" >22 %
CVN temp. 0°C >40 J
CVN temp.-20°C >27 J

Filo S2
Typical Chemical Properties (As Welded)
C 0.025-0.05, Mn 1.10-1.50, Si 0.60-1.00, Cu <0.35, S 0.020, P 0.030

Typical Mechanical Properties (As Welded)
Tensile Strength >520 MPa
Yield Strength >400 MPa
Elongation in 2" >22 %
CVN temp. 0°C >50 J
CVN temp.-20°C >27 J

Re-baking performed at 350°C for two hours in a vented oven, to obtain diffusible hydrogen 5 ml/100 gr max